5CrNiMo鋼具有良好的韌性、強度和高耐磨性，屬熱作模具鋼。它在室溫和500～600℃時的力學(xué)性能幾乎相同。在加熱到500℃時，仍能保持住HB300左右的硬度。由于鋼中含有鉬，因而對回火脆性并不敏感。從600℃緩慢冷卻下來以后，沖擊韌性僅稍有降低。
化學(xué)成份
碳 C ：0.50～0.60
硅 Si：≤0.40
錳 Mn：0.50～0.80
硫 S ：≤0.030
磷 P ：≤0.030
鉻 Cr：0.50～0.80
鎳 Ni：1.40-1.80
銅 Cu：允許殘余含量≤0.30
鉬 Mo：0.15～0.30
硬度：退火,241～197HB,壓痕直徑3.9～4.3mm
技術(shù)參數(shù)
淬火后 ：58
淬火溫度℃ ：830～860
交貨狀態(tài) ：退火HB≤241
冷卻劑 ：油Oil
自由鍛件公司哪家好，就找唐山盛通鍛造有限公司。
5CrNiMo steel has good toughness, strength and high wear resistance, and is a hot work die steel. It has almost the same mechanical properties at room temperature and 500 to 600 °C. When heated to 500 ° C, it can still maintain the hardness of HB300. Because steel contains molybdenum, it is not sensitive to temper brittleness. After slowly cooling from 600 ° C, the impact toughness was only slightly reduced.
chemical composition
Carbon C: 0.50~0.60
Silicon Si: ≤ 0.40
Mn: 0.50 to 0.80
Sulfur S :≤0.030
Phosphorus P :≤0.030
Chromium Cr: 0.50~0.80
Nickel Ni: 1.40-1.80
Copper Cu: Allowable residual content ≤ 0.30
Molybdenum Mo: 0.15~0.30
Hardness: Annealed, 241 ~ 197HB, indentation diameter 3.9 ~ 4.3mm
technical parameter
After quenching: 58
Quenching temperature °C: 830 ~ 860
Delivery status: Annealing HB≤241
Coolant : Oil Oil