JASO M610日本工業(yè)協(xié)會(huì)汽車(chē)零部件外涂層腐蝕試驗(yàn)方法
點(diǎn)擊次數(shù)：2171 發(fā)布時(shí)間：2022-4-12
JASO M610日本工業(yè)協(xié)會(huì)汽車(chē)零部件外涂層腐蝕試驗(yàn)方法
This standard specifies a test method for examining the cosmetic corrosion of metallic automotive parts and their surface treatments. It is cyclic in nature, i.e.; test specimens are exposed to changing climates over time.
Test specimens are placed in an enclosed chamber and exposed to a changing climate that comprises of the following 3 part repeating cycle. 2.0 hours exposure to salt spray at +35C according JIS Z 2371. This is followed by 4.0 hours of air drying in a climate of 20 to 30%RH at +60C. This is followed by 2.0 hours exposure to a condensing water climate (wetting) of 95 to 100%RH at +50C. The number of cycle repeats and therefore the test duration is variable.
The maximum transition times between each part of the test cycle are also specified as follows:
From salt spraying to air drying within 30 minutes.
From air drying to wetting within 15 minutes.
From wetting to salt spraying within 30 minutes.
Please see elsewhere in this document for details of JIS Z 2371.
Chamber volumes of less than 400 Litres are not permitted by this test standard.
This test is also referred to as a Cyclic Corrosion Test, often abbreviated to CCT.
項(xiàng)目 | 名稱(chēng) | 條件 |
1 | 鹽霧測(cè)試 |
|
| 1、 溫度 2、 鹽水比例 | 1、 35±1 ℃ 2 、5%±0.5% 其他條件參考 JIS 2371 |
2 | 干燥 |
|
| 1溫度 2濕度 | 1、 60±1℃ 2、 20~30% RH |
3
| 濕潤(rùn)（冷凝） |
|
| 1、溫度 2、濕度 | 1、 50±1℃ 2、95% RH以上 |
5 | 周期持續(xù)時(shí)間和內(nèi)容 | 8小時(shí) 鹽霧：2小時(shí) 干燥：4小時(shí) 潤(rùn)濕：2小時(shí) （包括每次變化的時(shí)間） |
6 | 改變條件所需的時(shí)間（在達(dá)到條件后達(dá)到所需溫度和相對(duì)濕度所需的時(shí)間） | 從鹽霧到干燥：30分鐘內(nèi) 從干燥到濕潤(rùn)：15分鐘內(nèi) 從潤(rùn)濕到噴霧：30分鐘內(nèi) （原則上是瞬間噴灑） |
7 |
| |
8 | 試件夾持角 | 垂直線(xiàn) 15-20° |
Chamber volumes of less than 400 Litres are not permitted by this test standard.
內(nèi)部尺寸小于400升的試驗(yàn)箱不允許通過(guò)該試驗(yàn)標(biāo)準(zhǔn)